1.0570, DIN St52-3N, S355J2G3
IHE MMADỤ N'ỤWA
This ọkwa nke ígwèbụ carbon manganese, nnukwu mkpụrụ na-abụghị alloy ígwè. A na-akpọ ya S355 n'ihi na nkezi kacha nta maka ihe a bụ 355 Mpa. Dị ka ígwè structural, ọ nwere ezigbo ike na weldability. Enwere ike ịgbanye ya ngwa ngwa na nchara ndị ọzọ nwere ike weld. Maka obere carbon ya, ọ nwere ezigbo ihe na-emepụta oyi. A na-enye S355J2G3 n'ọnọdụ kwesịrị ekwesị.
Nhọpụta site na Standards
Mat. Mba. | SITE | N'ime | AISI |
1.0570 | St52-3N | - | - |
Ngwakọta kemịkalụ (n'ịdị arọ%)
C | Na | Mn | Cr | Mo | N'ime | N'ime | N'ime | Ndị ọzọ |
max. 0.22 | max. 0.55 | max. 1.60 | - | - | - | - | - | - |
Nkọwa nchara arụrụ arụ na-adịghị mma. Ngwa nchara arụrụ arụ a na-ahụkarị maka ọgbakọ welded, RỌ bụ>355 N/mm2 . Ekwenyere na ike na 0O C. Enwere ike iji ya mee ihe maka ihe owuwu na-arụ ọrụ nke ọma. Njirimara anụ ahụ (nkezi ụkpụrụ) na ọnọdụ okpomọkụ Modul nke ngbanwe [103x N/mm2]: 210 njupụta [g/cm3]: 7.80 Igwe ọkụ na-ekpo ọkụ dị nro ruo 650-700O C, dị jụụ nwayọọ nwayọọ. Hardening Harden site na okpomọkụ nke 860-890O C na-esote mmanụ ma ọ bụ imenyụ mmiri. Ọkụ na-eme ka ọ dị mma: 860-890OC. Igwe ọkụ na-emepụta okpomọkụ: 1050-850OC. Machinability Machinability dị mma, kwadoro na 90% nke alloy 1112 ejiri mee ihe dị ka 100% ígwè ígwè.