1.0601, DIN C60, AISI 1060
IHE MMADỤ N'ỤWA
C60ígwè bụ ihe na-adịghị alloyed ọkara carbon engineeringígwè nke nwere 0.57% -0.65% Carbon dị ka ọkọlọtọ EN10083. O nwere njirimara yiri nke C55 carbon steel nke nwere ike siri ike na ike dị elu mgbe ọ gbasasịrị.C60 siri ike ịgbado, na machinability adịghị mma n'ihi nnukwu ọdịnaya carbon. A na-enyekarị ígwè a n'ọnọdụ adịghị agwọ ya ma ọ bụ nke a na-ahazi.
Nhọpụta site na Standards
Mat. Mba. | SITE | N'ime | AISI |
1.0601 | C60 | - | 1060 |
Ngwakọta kemịkalụ (n'ịdị arọ%)
C | Na | Mn | Cr | Mo | N'ime | N'ime | N'ime | Ndị ọzọ |
0.61 | max. 0.40 | 0.75 | max. 0.40 | max. 0.10 | max. 0.40 | - | - | (Cr+Mo+Ni)= max. 0.63 |
Nkọwa C60 bụ otu n'ime ihe ndị nwere carbon dị elu (0.60%) nchara. Ọ na-esiri ike ịmepụta karịa ọkwa carbon dị ala. Ngwa Ngwa gụnyere ngwa aka dị ka screwdrivers, ngwa nju na ihe ndị yiri ya. Njirimara anụ ahụ (nkezi ụkpụrụ) na ọnọdụ okpomọkụ Modul nke ngbanwe [103x N/mm2]: 210 njupụta [g/cm3]: 7.85 Thermal conductivity [W/mK]: 46.6 Electric resistivity [Ohm mm2/ m]: 0.127 Specific ike okpomọkụ[J/gK]: 0.46 Ọnụọgụ nke Linear Thermal Expansion 10-6CelsiusC-1
20-100°C | 20-200°C | 20-300°C | 20-40°C | 20-500°C |
11.1 | 12.1 | 12.9 | 13.5 | 13.9 |
Okpomọkụ na-ekpo ọkụ dị nro ruo 680-710° C, dị jụụ nwayọọ n'ime ọkụ. Nke a ga-emepụta oke brinell siri ike nke 241. Normalizing Normalizing okpomọkụ: 820-86 ° C/ikuku. Hardening hardden si na okpomọkụ nke 800-840° C na-esote mmiri ma ọ bụ mmanụ quenching. Ọkụ na-ekpo ọkụ: 550-660° C/ikuku. Ngwongwo arụrụ arụ na ọnọdụ iwe ọkụ siri ike
Dayameta (mm) | 0.2% mgbakasị ihe akaebe (N/mm²) | Ike ntanye (N/mm²) | Elongation A5(%) | Mbelata Z (%) |
ruo 16 | 570 | 830-980 | 11 | 20 |
17-40 | 490 | 780-930 | 13 | 30 |
41-100 | 450 | 740-890 | 14 | 35 |
Ngwongwo arụrụ arụ na ọnọdụ ahaziri ahazi
Dayameta (mm) | 0.2% mgbakasị ihe akaebe (N/mm²) | Ike ntanye (N/mm²) | Elongation A5(%) |
ruo 16 | min. 380 | min. 710 | min. 10 |
17-100 | min. 340 | min. 670 | min. 11 |
101-250 | min. 310 | min. 650 | min. 11 |
Eserese Okpomọkụ Na-ekpo ọkụ - Mechanical Njirimara
Okpomọkụ na-akpụ ọkụ ọkụ: 1100-800° C. Machinability Machinability nke C60 na ihe niile nke carbon steel dị elu adịghị mma. C60 ọnụego na 55 ruo 60 % nke AISI 1112 ígwè nke a na-ewere 100% machinable. Nguzogide corrosion ígwè a anaghị eguzogide corrosion. ọ ga-agba nchara ma echekwaghị ya. Enwere ike ịgbado ịgbado ọkụ C60 site na usoro niile a na-ahụkarị. Otú ọ dị, ekwesịrị iji ma tupu ikpo ọkụ na mgbe ọkụ gasịrị mgbe ị na-agbado site na usoro akwadoro. Kpoo ọkụ na 260 ruo 320 °C na post-okpomọkụ na 650 ruo 780 °C. Oyi na-arụ ọrụ oyi na-arụ ọrụ siri ike ọbụna na ọnọdụ annealed ọ bụ ezie na ọ nwere ike ime ya site na usoro omenala mana ọ chọrọ ike dị ukwuu karịa obere carbon steels.