1.0570, DIN St52-3N, S355J2G3
GENERAL abuda
This ite ti irinni erogba manganese, ga ikore ti kii alloy, irin. O pe ni S355 nitori apapọ ikore ti o kere julọ fun ohun elo yii jẹ 355 Mpa. Bi awọn kan igbekale irin, o ni o ni o tayọ agbara ati weldability. O le wa ni imurasilẹ welded si miiran weldable irin. Fun deede erogba kekere rẹ, o ni awọn ohun-ini didan tutu to dara. S355J2G3 ni gbogbo igba ti a pese ni ipo deede.
Oya nipa Standards
Matt. Rara. | LATI | IN | AISI |
1.0570 | St52-3N | - | - |
Iṣọkan Kemikali (ni iwuwo%)
C | Ati | Mn | Kr | Mo | Ni | IN | IN | Awọn miiran |
o pọju. 0.22 | o pọju. 0.55 | o pọju. 1.60 | - | - | - | - | - | - |
Apejuwe Unalloyed igbekale irin. Awọn ohun elo irin igbekalẹ to wọpọ fun awọn apejọ welded, ROun ni> 355 N/mm2 . Ni idaniloju lile lile ni 0O C. O le ṣee lo fun statically ati ki o dynamically tenumo constructions. Awọn ohun-ini ti ara (awọn iye apapọ) ni iwọn otutu ibaramu Modulus ti rirọ [103x N/mm2]: 210 iwuwo [g/cm3]: 7.80 Asọ Annealing Heat to 650-700O C, dara laiyara. Hardening Harden lati iwọn otutu ti 860-890O C atẹle nipa epo tabi omi quenching. Tempering Normalizing otutu: 860-890OC. Forging Gbona iwọn otutu: 1050-850OC. Ṣiṣe ẹrọ ẹrọ ti o dara, ti a ṣe ni 90% ti 1112 alloy ti a lo bi 100% ẹrọ ti o ni iwọn irin.